Mechanism of the anomalous temperature dependence of coercivity in Sm(Co,Fe,Cu,Zr)[subscript]z high-temperature magnets
(American Institute of Physics, 2006-01-24)
Coercivity mechanism of the precipitation-hardened Sm(Co,Fe,Cu,Zr)z high-temperature magnets was found to vary with temperature by measurements of reversible magnetization. The magnetization reversal is mainly controlled ...
Do thermal fluctuations influence the recoil loops of nanocomposite magnets?
(American Institute of Physics, 2008-07-11)
An exchange-coupled FePt/Fe3Pt nanocomposite system with well defined hard/soft two-phase morphology was prepared by reducing chemically synthesized FePt/Fe3O4 bimagnetic nanoparticles. It was interesting to observe that ...
Phase Transformation and Magnetic Hardening in Isolated FePt Nanoparticles
(IEEE, 2009-03-31)
Isolated monodisperse L1[subscript]0 FePt nanoparticles coated by carbon were obtained by adding enough surfactants that decomposed into carbon after the chemical synthesis and postannealing of the A1 FePt nanoparticles. ...
Phase Transformation and Magnetic Hardening in Isolated FePt Nanoparticles
(IEEE XploreIEEE, 2009-07)
Isolated monodisperseL10 FePt nanoparticles coated
by carbon were obtained by adding enough surfactants that decomposed
into carbon after the chemical synthesis and postannealing
of the A1 FePt nanoparticles. The effect ...
Bulk FePt/Fe3Pt nanocomposite magnets prepared by spark plasma sintering
(AIP, 2007)
FePt/Fe3Pt bulk nanocomposite magnets have been prepared by the spark plasma sintering of chemically synthesized FePt and Fe3O4 nanoparticles under 100 MPa at 400–600 °C. It was found that the phase transition of the FePt ...
Hard magnetic FePt nanoparticles by salt-matrix annealing
(AIP, 2006)
To transfer face-centered-cubic (fcc) FePt nanoparticles to the face-centered-tetragonal (fct) phase with high magnetic anisotropy, heat treatments are necessary. The heat treatments lead to agglomeration and sintering of ...
Bulk FePt-based nanocomposite magnets with enhanced exchange coupling
(AIP, 2007)
High density bulk FePt/Fe3Pt nanocomposite magnets have been prepared by high-pressure warm compaction of chemically synthesized FePt and Fe3O4 nanoparticles. It is found that the density increases with the compaction ...
Structural phase transition and ferromagnetism in monodisperse 3 nm FePt particles
(AIP, 2007)
FePt nanoparticles with a size of 3 nm and thermally stable room-temperature ferromagnetism are investigated. The monodisperse nanoparticles were prepared by chemical synthesis and a salt-matrix annealing technique. ...
Rapid thermal annealing of FePt nanoparticles
(AIP, 2008-07-01)
We report a systematic study on rapid thermal annealing (RTA) of FePt nanoparticles. FePt particles with an average size of 8 nm were synthesized by a chemical solution method, and then annealed using RTA and conventional ...
Microstructures and magnetic alignment of L10 FePt nanoparticles
(AIP, 2009)
Chemically ordered FePt nanoparticles were obtained by high temperature annealing a mixture of FePt particles with NaCl. After the NaCl was removed with de-ionized water, the transformed FePt nanoparticles were redispersed ...