Observation of L1[subscript]0-like chemical ordering in a decahedral FePt nanoparticle by C[subscript]s-corrected high resolution transmission electron microscopy
(American Institute of Physics, 2009-03-09)
The state of the chemical ordering in a decahedral FePt nanoparticle was studied using aberration corrected high resolution transmission electron microscopy. With the reduced image delocalization effect as a result of ...
Fabrication of bulk nanocomposite magnets via severe plastic deformation and warm compaction,
(American Institute of Physics, 2010-03-10)
We demonstrate that a SmCo/FeCo based hard/soft nanocomposite material can be fabricated by distributing the soft magnetic α-Fe phase particles homogeneously in a hard magnetic SmCo phase through severe plastic deformation. ...
Bulk FePt/Fe3Pt nanocomposite magnets prepared by spark plasma sintering
(American Institute of Physics, 2007-04-27)
FePt/Fe3Pt bulk nanocomposite magnets have been prepared by the spark plasma sintering of chemically synthesized FePt and Fe3O4 nanoparticles under 100 MPa at 400–600 °C. It was found that the phase transition of the FePt ...
Bimagnetic nanoparticles with enhanced exchange coupling and energy products
(American Institute of Physics, 2009-01-06)
Bimagnetic FePt/Fe3O4 nanoparticles with core/shell or heterodimer structure have been prepared using a sequential synthetic method. The dimension of both FePt and Fe3O4 was tuned by varying the synthesis parameters. The ...
Rapid thermal annealing of FePt nanoparticles
(American Institute of Physics, 2008-07-11)
We report a systematic study on rapid thermal annealing (RTA) of FePt nanoparticles. FePt particles with an average size of 8 nm were synthesized by a chemical solution method, and then annealed using RTA and conventional ...
First-principles prediction of enhanced magnetic anisotropy in FeCo alloys
(American Institute of Physics, 2008-02-04)
The structural, electronic, and magnetic properties of FeCo alloys were studied by first-principles calculations. It has been found that the alloys prefer chemically noncubic geometries in a wide composition range. This ...
Temperature- and magnetic-field-induced phase transitions in Fe-rich FePt alloys
(American Institute of Physics, 2007-06-01)
Structural and magnetic properties of the FexPt100-x (x=78–88) alloys have been investigated. It is found that for all of the investigated compositions, a phase transition occurs from the disordered γ phase to the ordered ...
Structural phase transition and ferromagnetism in monodisperse 3 nm FePt particles
(American Institute of Physics, 2007-08-30)
FePt nanoparticles with a size of 3 nm and thermally stable room-temperature ferromagnetism are investigated. The monodisperse nanoparticles were prepared by chemical synthesis and a salt-matrix annealing technique. ...
High thermal stability of carbon-coated L1[subscript]0-FePt nanoparticles prepared by salt-matrix annealing
(Institute of Applied Physics, 2008-02-08)
Monodisperse L10-FePt nanoparticles with size ranging from 3 to 8 nm were prepared by the salt-matrix annealing method. It was observed that the annealed particles have high thermal stability—no sintering occurred even ...
Curie temperatures of annealed FePt nanoparticle systems
(American Institute of Physics, 2007-03-28)
The chemically synthesized FexPt100-x nanoparticles with controlled compositions were annealed to transfer the disordered face-centered-cubic structure to the ordered structure. It was found that the L10 FePt structure can ...