Observation of L1[subscript]0-like chemical ordering in a decahedral FePt nanoparticle by C[subscript]s-corrected high resolution transmission electron microscopy
(American Institute of Physics, 2009-03-09)
The state of the chemical ordering in a decahedral FePt nanoparticle was studied using aberration corrected high resolution transmission electron microscopy. With the reduced image delocalization effect as a result of ...
Effect of thermal fluctuations on the recoil loops of SmCo5[subscript]/Fe nanocomposite system
(American Institute of Physics, 2009-02-13)
The correlation between the recoil loop openness and the activation volume has been studied for the SmCo5/α-Fe nanocomposite powder material prepared by mechanical alloying. The α-Fe phase content in the nanocomposite ...
Bimagnetic nanoparticles with enhanced exchange coupling and energy products
(American Institute of Physics, 2009-01-06)
Bimagnetic FePt/Fe3O4 nanoparticles with core/shell or heterodimer structure have been prepared using a sequential synthetic method. The dimension of both FePt and Fe3O4 was tuned by varying the synthesis parameters. The ...
Grain boundary contribution to recoil loop openness of exchange-coupled nanocrystalline magnets
(American Institute of Physics, 2009-04-29)
It has been well known that recoil loop openness is related to soft-phase presence in exchange-coupled hard-soft nanocomposite magnets. Our study on recoil loop openness of exchange-coupled nanocrystalline magnets (both ...
Shape control of FePt nanocrystals
(American Institute of Physics, 2009-04-06)
: FePt nanocrystals were prepared by simultaneous reduction of platinum acetylacetonate and thermal decomposition of iron pentacarbonyl in properly chosen solvents/surfactants. A variety of FePt nanocrystals, including ...
Phase Transformation and Magnetic Hardening in Isolated FePt Nanoparticles
(IEEE, 2009-03-31)
Isolated monodisperse L1[subscript]0 FePt nanoparticles coated by carbon were obtained by adding enough surfactants that decomposed into carbon after the chemical synthesis and postannealing of the A1 FePt nanoparticles. ...
Phase Transformation and Magnetic Hardening in Isolated FePt Nanoparticles
(IEEE XploreIEEE, 2009-07)
Isolated monodisperseL10 FePt nanoparticles coated
by carbon were obtained by adding enough surfactants that decomposed
into carbon after the chemical synthesis and postannealing
of the A1 FePt nanoparticles. The effect ...
Microstructures and magnetic alignment of L10 FePt nanoparticles
(AIP, 2009)
Chemically ordered FePt nanoparticles were obtained by high temperature annealing a mixture of FePt particles with NaCl. After the NaCl was removed with de-ionized water, the transformed FePt nanoparticles were redispersed ...